FIB milling using Ga ions is known to be accompanied by implantation, multiplication of material defects, material property modification (e.g. amorphisation), inelastic shrinking/swelling and residual stress generation. These...
FIB-DIC ringcore milling is an attractive semi-destructive method of measuring microscopic residual stress. Ensuring the accuracy and reliability of DIC analysis of sample surface deformation is critical for correct stress...
FIB-DIC ringcore milling is an attractive semi-destructive method of measuring microscopic residual stress. Ensuring the accuracy and reliability of DIC analysis of sample surface deformation is critical for correct stress...
FIB milling using Ga ions is known to be accompanied by implantation, multiplication of material defects, material property modification (e.g. amorphisation), inelastic shrinking/swelling and residual stress generation. These...
Fatigue Crack Growth Rate (FCGR) is altered by a single anomalous load exceeding cyclic maximum (Overload) or compressive load below cyclic minimum (Underload). The authors study fatigue crack acceleration due to a single...
High energy 2D X-ray powder diffraction experiments are widely used for lattice strain measurement. The 2D to 1D conversion of diffraction patterns is a necessary step used to prepare the data for full pattern refinement, but...
High energy 2D X-ray powder diffraction experiments are widely used for lattice strain measurement. The 2D to 1D conversion of diffraction patterns is a necessary step used to prepare the data for full pattern refinement, but...
Precious metals, such as platinum group metals (PGMs) with distinct catalytic activity, are widely used as active components in various industrial catalysts. It is, therefore, highly desirable to recover these valuable...
Fatigue Crack Growth Rate (FCGR) is altered by a single anomalous load exceeding cyclic maximum (Overload) or compressive load below cyclic minimum (Underload). The authors study fatigue crack acceleration due to a single...
|
|< |
< |